Description

Cores are cut using a drill with a hollow barrel tipped with industrial diamonds. The whole rig has to be firmly fixed in position by weights, anchor bolts, vacuum pads or bracing against other parts of the structure. The preferred core diameter for strength testing is not defined in BS EN 12504-1, BS EN 13791 or BS 6089 but the diameter should be at least 3.5 x the maximum aggreagte size.  Sometimes even smaller diameter cores have to be used for strength testing. In this case the strength results can be more variable and a greater number of cores should be extracted. For strength testing, the length to diameter ratio should be between 1 and 2 and preferably between 1 and 1.2. When cores are received in the laboratory they may be examined for degree of compaction, cracks, voids, honeycombing and the presence of reinforcement.

Before testing cores for strength, they have to be trimmed to length and the ends prepared so that they are flat and perpendicular to the longitudinal axis. This is achieved by grinding or, more usually, capping with high alumina cement (calcium aluminate cement) mortar or a sulphur/sand mixture. Cores should be tested in a dry state. This is a air dry, not oven dry. If tested wet a small positive correction to the strength is made.



Typical core sample
Acknowledgement The Concrete Society
Bookshop

Click image or title
for more information
In situ concrete strength
- an investigation into the relationship between core strength and stan
TR54 Diagnosis of deterioration in concrete structures
- identification of defects, evaluation an
Assessment of in-situ concrete strength using data obtained from core testing
 
Sitemap  -  Links